17-7 Uamea Uamea, Coil, Pepa, Uaea, AMS 5528 (CONDA), AMS 5529 (COND C), ASTM A693, MIL-S25043
Fa'amatalaga
Ituaiga 17-7PH® Fua Fa'ama'a'a Alloy o se semi-austenitic u'amea u'amea lea e austenitic i le tulaga annealed, ae martensitic i le tulaga malo. Ituaiga 17-7PH® e maua ai le malosi maualuga ma le ma'a'a'a, sili ona lelei le vaivai, lelei le fa'a'a'a'a ma fa'aletonu la'ititi i luga ole vevela. E faigofie ona fausia i le tulaga fa'afefeteina, ona fa'ama'a'a ai lea i tulaga maualuga o le malosi e ala i togafitiga vevela faigofie i Tulaga RH 950 ma le TH 1050. O le maualuga maualuga o le Tulaga CH 900 e ofoina atu le tele o mea lelei pe a fa'ataga le fa'agata ma le fa'aogaina. I lona tulaga vevela, o lenei u'amea e maua ai mea fa'ainisinia fa'apitoa i le vevela e o'o atu i le 900 °F (482 °C).
KEMILISI FA'ATAU
Carbon: 0.090 maualuga
Manganese: 1.00 maualuga
Silikoni: 1.00 maualuga
Chromium: 16.00-18.00
Nikeli: 6.50- 7.75
Alumini: 0.75-1.50
Phosphorus: 0.040 maualuga
Sulfur: 0.030 maualuga
Uamea: Paleni
METOTIA FAALETINO
Malosi: (Cond. A): 0.282 lbs/in3 7.80 g/cm3
Tete'e Fa'aeletise: (microhm-cm) (tulaga uma): 60 °F (20 °C): 80
Amioga vevela: BTU/hr/ft2/ft/°F (W/m•K)
I le 300 °F (149 °C): 9.5 (16.5)
Fua Fa'atatau o le Fa'alauteleina o le vevela: in/inl°F (µm/m•K): (Cond. A):
70 -200 °F (21 -93 °C): 8.5 x 10-5 (15.3)
70 -400 °F (21 -204 °C): 9.0 x 10-5 (16.2)
70 -600 °F (21 -315 °C): 9.5 x 10-5 (17.1)
70 -800 °F (21 -427 °C): 9.6 x 1 o-6 (16.0)
Modulus o Elasticity: ksi (MPa)
29 x 103 (200 x 103) i le vevesi
Malosi fa'amaneta:
Fa'apipi'i: E vaivai le ferromagnetic
Fa'asalaina vevela: Malosi ferromagnetic
FOFOGA
Aveese Coil
- 17-7PH uamea uamea
- 17-7PH i'a uamea uamea
- 17-7PH Lipine uamea uamea
Oloa uaea
- 17-7PH uaea uamea uamea fau & uaea Profile
- 17-7PH uaea lapotopoto lapotopoto
- 17-7PH uaea uamea uamea mafolafola
- 17-7PH uaea u'amea uamea sikuea
Fa'atinoga
Fa'agaioiina Meatotino Fa'ainisinia I le vevela o le potu
Fua Fa'atatau:<.010 inisi
Malosi Sili: 150 KSI maualuga (1035 MPa maualuga)
Malosi fua (0.2% offset): 65 KSI maualuga (450 MPa maualuga)
Elongation: Consult Ulbrich Technical Services
Fua Va'aiga: > .010 inisi
Malosi Sili: 150 KSI maualuga (1035 MPa maualuga)
Malosi fua (0.2% offset): 55 KSI maualuga (380 MPa maualuga)
Elongation: 20% min
Malosi: Rb 92 maualuga
Tulaga masani C
Malosi Sili: 200 KSI min (1380 MPa min)
Malosi e maua mai (0.2% offset): 175 KSI min (1205 MPa min)
Fa'aumiumi: 1 % min
Ma'a'a: Toe 41 min (manu'ai)
FA'ATA'IGA FA'ATA'ITA'I FA'AVAE:
Fa'afeso'ota'i Au'aunaga Fa'atekinisi a Ulbrich pe a mana'omia le ita e ese mai le Tulaga C.
TOTOGI O LE VAVA O LE 17-7PH UA'U'U'U
TH 1050 masani
Malosi Sili: 180 KSI min (1240 MPa min)
Malosi e maua ai: (0.2% Offset) 150 KSI min (1034 MPa min)
Elongation: Consult Ulbrich Technical Services
Malosi: Toe 38 min
RH950 masani
Malosi Sili: 210 KSI min (1450 MPa min)
Malosi e maua ai: (0.2 Offset) 190 KSI min (1310 MPa min)
Elongation: Consult Ulbrich Technical Services
Malosi: Toe 44 min
CH900 masani
Malosi Sili: 240 KSI min (1655 MPa min)
Malosi e maua ai: (0.2% Offset) 230 KSI min (1586 MPa min)
Fa'aumiumi: 1 % min
Malosi: Toe 46 minu (fa'amoemoe)
MEATOTOGA FAAOPOOPO
TETE'E ELE'A O LE 17-7PH STAINLESS STEEL
Va'ai ile NACE (National Association of Corrosion Engineers) mo fautuaga.